In this study, the fatigue behavior of (±45°)3 filament-wound composite pipes with a surface crack under alternating internal pressure was investigated. Glass-reinforced plastic (GRP) pipes were made of E-glass/epoxy and tested in the open-ended condition. The pipes had a surface crack with a notch–aspect ratio of a/c = 0.2 and notch-to-thickness ratios of a/t = 0.25, 0.38, or 0.50 in the axial direction. Tests were carried out in accordance with ASTM D2992. This standard offers 25 cycles/min and a load ratio of R = 0.05. Tests were performed at three different load levels: 50%, 40%, and 30% of ultimate hoop stress. Whitening, leakage, and final failure of GRP pipes were observed, and fatigue test results were presented by means of S–N curves.
TarakçioğluNSamanciAArikanHAkdemirA. The fatigue behavior of (±55°)3 filament wound GRP pipes with a surface crack under internal pressure. Composite Structures2007; 80: 207–211.
2.
RousseauJPerreuxDVerdiereN. Influence of winding patterns on the damage behavior of filament-wound pipes. Composite Science and Technology1999; 59: 1439–1449.
3.
FerryLPerreuxDRousseauJRichardF. Interaction between plasticity and damage in the behavior of [+,−]n fiber reinforced composite pipes in biaxial loading (internal pressure and tension). Composite Part B Eng1998; 29: 715–723.
4.
RichardFPerreuxD. A reliability method for optimization of ϕ fiber reinforced composite pipes. Reliability Engineering and System Safety2000; 68: 53–59.
5.
JosephEPerreuxD. Fatigue behavior of glass–fiber/epoxy matrix filament-wound pipes. Composite Science and Technology1994; 52: 469–480.
6.
PerreuxDJosephD. The effect of frequency on the fatigue performance of filament wound pipes under biaxial fatigue experimental results and damage model. Composite Science and Technology1997; 57: 353–364.
7.
EllyinFMartensM. Biaxial fatigue behavior of a multidirectional filament-wound glass–fiber/epoxy pipe. Composite Science and Technology2000; 61: 491–502.
8.
MartensMEllyinF. Biaxial monotonic behavior of a multidirectional filament-wound glass–fiber/epoxy pipe. Composites Part A2000; 31: 1001–1014.
9.
WolodgoJ, Biaxial fatigue and leakage characteristics of fiber reinforced composite tubes. PhD. Thesis, University of Alberta, Canada, 1999.
10.
KaynakCMatO. Uniaxial fatigue behavior of filament-wound glass–fiber/epoxy tubes. Composite Science and Technology2001; 61: 1833–1840.
11.
AkdemirATarakçioğluNAvciA. Stress corrosion crack growth in glass–polyester composites with surface crack. Composites Part B2000; 32: 123–129.
12.
TarakçioğluNAkdemirAAvciA. Strength of filament wound GRP pipes with surface crack. Composites Part B2001; 32: 131–138.
13.
TarakçioğluNGemiLYapiciA. Fatigue failure behavior of glass/epoxy (±55°) filament wound pipes under internal pressure. Composite Science and Technology2005; 65: 703–708.
14.
AvciASahinOSTarakçioğluN. Fatigue behavior of surface cracked filament wound pipes with high tangential strength in corrosive environment. Composites Part A2006; 38: 1192–1199.
15.
SamanciAAvciATarakçioğluNSahinOS. Fatigue crack growth of filament wound GRP pipes with a surface crack under cyclic internal pressure. Journal of Material Science2008; 48: 5569–5573.
16.
GemiLTarakçioğluNAkdemirASahinOS. Progressive fatigue failure behavior of glass/epoxy (±75°)2 filament-wound pipes under pure internal pressure. Materials and Design2009; 30: 4293–4298.
17.
ArikanH. Failure analysis of (±55°)3 filament wound composite pipes with an inclined surface crack under static internal pressure. Composite Structures2010; 92: 182–187.
18.
ErkalSSaymanOBenliS. Fatigue damage in composite cylinders. Polymer Composites2010; 31: 707–713.
SaymanO. Analysis of multi-layered composite cylinders under hydrothermal loading. Composites Part A Applied Science and Manufacturing2005; 36: 923–933.
21.
Standard practice for obtaining hydrostatic or pressure design basis for “fiberglass” (glass-fiber-reinforced thermosetting resin) pipe and fittings. American Society for Testing Materials (ASTM) designation: D2992-91.