Microplasma spray equipment to deposit calcium phosphate ceramic (CaP) coatings has been developed. Fifty-six titanium implants were inserted into the mandibles of 7 adult beagle dogs. The implants were either acid-etched (NC), conventionally plasma-sprayed (PS), micro-plasma-sprayed (MPS), or micro-plasma-sprayed (aMPS) only at the apical part. After 6 weeks, implants in one half of the mandible were subjected to load. Fifty-two weeks thereafter, the animals were killed. Regardless of load, bone healing was comparable for all surfaces tested. It was concluded that loading of MPS CaP-coated implants evokes a favorable bone response, and that the bone response does not differ from that of PS CaP-coated implants. However, functional loading of PS as well as MPS CaP-coated implants might be associated with increased crestal bone maintenance as compared with non-coated implants.
BlockMGardinerDAlmericoBNealC (2000). Loaded hydroxyapatite-coated implants and uncoated titanium-threaded implants in distracted dog alveolar ridges. Oral Surg Oral Med Oral Pathol Oral Radiol Endod89:676-685.
2.
BloebaumRMerrellMGustkeKSimmonsM (1991). Retrieval analysis of a hydroxyapatite-coated hip prosthesis. Clin Orthop Relat Res267:97-102.
3.
BorisovYVojnarovichSUlianchichNJansenJWolkeJ (2002). Investigation of bioceramic coatings produced by microplasma spraying. Paton Welding J9:4-6.
4.
BrettPHarleJSalihVMihocROlsenIJonesF. (2004). Roughness response genes in osteoblasts. Bone35:124-133.
5.
BrunskiJB (1999). In vivo bone response to biomechanical loading at the bone/dental-implant interface. Adv Dent Res13:99-119.
6.
BrunskiJBCurreyJAHelmsJALeuchtPNanciAWazenR (2009). The healing bone-implant interface: role of micromotion and tissue related strain levels in tissue. In: Osseointegration and dental implants. Based on the proceedings of the Toronto Osseointegration Conference Revisited, May 8–10, 2008. JokstadA, editor. Toronto, Canada: Wiley-Blackwell Publishing Co., Chapter 11, pp. 205-212.
7.
CaulierHvan der WaerdenJPPaquayYCWolkeJGKalkWNaertI. (1995). Effect of calcium phosphate (Ca-P) coatings on trabecular bone response: a histological study. J Biomed Mater Res29:1061-1069.
8.
CaulierHVercaigneSNaertIvan der WaerdenJPWolkeJGKalkW. (1997a). The effect of Ca-P plasma-sprayed coatings on the initial bone healing of oral implants: an experimental study in the goat. J Biomed Mater Res34:121-128.
9.
CaulierHvan der WaerdenJPWolkeJGKalkWNaertIJansenJA (1997b). A histological and histomorphometrical evaluation of the application of screw-designed calciumphosphate (Ca-P)-coated implants in the cancellous maxillary bone of the goat. J Biomed Mater Res35:19-30.
10.
CooleyDVan DellenABurgessJWindelerA (1992). The advantages of coated titanium implants prepared by radio-frequency sputtering from hydroxyapatite. J Prosthet Dent67:93-100.
11.
DhertWKleinCWolkeJVan der VeldeEDe GrootKRozingP (1991). A mechanical investigation of fluorapatite, magnesiumwhitlockite and hydroxylapatite plasma-sprayed coatings in goats. J Biomed Mater Res25:1183-1200.
12.
GarettoLPChenJParrAJRobertsWE (1995) Remodeling dynamics of bone supporting rigidly fixed titanium implants: A histomorphometric comparison in four species including humans. Implant Dent4:235-243.
13.
JansenJVan der WaerdenJWolkeJ (1993). Histologic investigation of the biologic behavior of different hydroxyapatite plasma-sprayed coatings in rabbits. J Biomed Mater Res27:603-610.
14.
JansenJHulshoffJWolkeJ (1999). Calcium phosphate (CaP) ceramic surface coatings and their significance. In: Proceedings of the 3rd European Workshop on Periodontology. Berlin: Quintessenz, pp. 73-88.
15.
JohanssonCAlbrektssonT (1987). Integration of screw implants in the rabbit. A 1-year follow-up of removal of titanium implants. Int J Oral Maxillofac Implants2:69-75.
16.
JunkerRMandersPWolkeJBorisovYJansenJ (2010a). Bone-supportive behavior of microplasma-sprayed CaP-coated implants: mechanical and histological outcome in the goat. Clin Oral Implants Res21:189-200.
17.
JunkerRMandersPWolkeJBorisovYJansenJ (2010b). Bone reaction adjacent to microplasma sprayed CaP-coated oral implants subjected to occlusal load; an experimental study in the dog. Clin Oral Implants Res (in press).
18.
Le GuéhennecLSoueidanALayrollePAmouriqY (2007). Surface treatments of titanium dental implants for rapid osseointegration. Dent Mater23:844-854.
19.
LeeJRouhfarLBeirneO (2000). Survival of hydroxylapatite-coated implants: a meta-analytic review. J Oral Maxillofac Surg58:1372-1379.
20.
LeeJKimSMoonSLimSOngJLeeK (2009). A short-term study on immediate functional loading and immediate nonfunctional loading implant in dogs: histometric evaluation of bone reaction. Oral Surg Oral Med Oral Pathol Oral Radiol Endod107:519-524.
MoyPRomanosGRoccuzzoM (2009). Loading protocols and biological response. In: Osseointegration and dental implants. Based on the proceedings of the Toronto Osseointegration Conference Revisited, May 8-10, 2008. JokstadA, editor. Toronto, Canada: Wiley-Blackwell Publishing Co., pp. 239-253.
23.
NovãesABJrSouzaSLde OliveiraPTSouzaAM (2002) Histomorpho-metric analysis of the bone-implant contact obtained with 4 different implant surface treatments placed side by side in the dog mandible. Int J Oral Maxillofac Implants17:377-383.
24.
OngJBesshoKCarnesD (2002). Bone response to plasma-sprayed hydroxylapatite and radiofrequent-sputtered calcium phosphate implants in vivo. Int J Oral Maxillofac Implants17:581-586.
25.
PiattelliAScaranoAPiattelliM (1998). Histologic observation of 230 reviewed dental implants: 8 years experience (1989–1996). J Periodontol69:178-184.
26.
RiveroDFoxJSkiporAUrbanRGalanteJ (1988). Calcium phosphate coated porous titanium implants for enhanced skeletal fixation. J Biomed Mater Res22:191-201.
27.
Schwartz-AradDMardingerOLevinLKozlovskyAHirshbergA (2005). Marginal bone loss pattern around hydroxylapatite-coated versus commercially pure titanium implants after up to 12 years of follow-up. Int J Oral Maxillofac Implants20:238-244.
28.
ThomasKCookS (1985). An evaluation of variable influencing implant fixation by direct bone apposition. J Biomed Mater Res19:875-901.
29.
Van BlitterswijkCBovellYFlachJLeendersHvan den BrinkIde BruijnJ (1993). Variations in hydroxylapatite crystallinity: effects on interface reactions. In: Hydroxylapatite coatings in orthopaedic surgery. GeesinkRGTManleyMT, editors. New York, NY: Raven Press, Ltd.
30.
YamamotoHShibataYTachikawaTMiyazakiT (2006). In vivo performance of two different hydroxyapatite coatings on titanium prepared by discharging in electrolytes. J Biomed Mater Res B Appl Biomater78:211-214.
31.
YushchenkoKBorisovYPereverzevYBalakinVSmithR (1995). Microplasma spraying. In: Thermal spraying—current status and future trends. Vol. 1. OhmoriA, editor. Osaka, Japan: High Temperature Society of Japan, pp. 273-274.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.